          您所在的位置:網站首頁 > > 產品中心 > 汽車線束絕緣材料 > PVC汽車線環保型105℃汽車原線料 W-0596, W-0597, W-0598
          環保型105℃汽車原線料 W-0596, W-0597, W-0598
          105℃Lead-free Automotive Wire Compound...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Product Description 產品描述
          105℃lead-free automotive wire compound is granular compound which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and adds plasticizer, stabilizer and other accessory ingredients. This product has excellent mechanical and physical properties, electrical property and good processability. It can meet RoHS Standard. The cables with it can meet LV112, VW60306, DIN72551 and other related standards. The highest working temperature is 105℃.
          環保型105℃汽車原線料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。產品具有良好的機械物理性能和電性能,加工性能優異,符合RoHS環保標準。制成電線后可以滿足LV 112、VW 60306、DIN 72551等相關標準,最高工作溫度為105℃。
           
          Product Details  產品明細
          Model
          牌號
          Application
          用途
          W-0596 >16mm2cables
          16mm2以上規格的電線
          W-0597 0.5mm2 ~6mm2 cables
          0.5mm2 ~6mm2及以規格的電線
          W-0598 ≤ 0.5mm2 cables
          0.5mm2及以下規格的電線
           
           
          Processing Indicator 加工工藝
          Recommend to use of single-screw extruders with L/D= 20-25.
          建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          Molding Temperature
          機頭溫度
          W-0596 / W-0597 165-185℃ 180-190℃
          W-0598 165-185℃ 185-190℃
           
           
          Physical and Electrical Properties 機械物理性能及電性能指標

          Item

          試驗項目

          Unit
          單位
          Molding Temperature
          技術要求
          W-0596 W-0597 W-0598
          Density
          比重
          \ 1.32±0.02 1.32±0.02 1.32±0.02
          Tensile Strength
          拉伸強度
          MPa ≥18.0 ≥18.0 ≥18.0
          Elongation at Break
          斷裂伸長率
          % ≥250 ≥250 ≥250
          200℃Thermal Stability
          200℃時熱穩定時間
          min ≥200 ≥200 ≥200
          20℃Volume Resistivity
          20℃時體積電阻率
          Ω.m ≥1×1011 ≥1×1011 ≥1×1011
          Dielectric Strength
          介電強度
          MV/m ≥22 ≥20 ≥20
          Brittle Temperature with Impact
          沖擊脆化溫度
          -25 -25 -25
          Hardness
          硬度
          Shore A 88±2 94±2 97±2
          Thermal Aging
          熱老化試驗
          \ 136℃×168h
          Tensile Strength Variation
          拉伸強度變化率
          % ±20 ±20 ±20
          Elongation Variation
          斷裂伸長率變化率
          % ±20 ±20 ±20