          您所在的位置:網站首頁 > > 產品中心 > 汽車線束絕緣材料 > PVC汽車線環保型125℃汽車原線料 W-2597, W-2598
          環保型125℃汽車原線料 W-2597, W-2598
          125℃ Lead-free Automotive Wire Compound...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Product Description 產品描述
          125℃lead-free automotive wire compound is granular compound which is manufactured through mixing, plasticizing and pelletizing processes. It regards advanced PVC resin as the basic raw materials, and adds plasticizer, stabilizer and other accessory ingredients. These products have excellent mechanical and physical properties, electrical property and good processability. They can meet RoHS Standard. The cables with them can meet T3 automotive wire requirements in NFR13-415 standards. The highest working temperature is 125℃.
          環保型125℃汽車原線料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。產品具有良好的機械物理性能和電性能,加工性能優異,符合RoHS環保標準。制成電線后可滿足ISO 6722 中T3型汽車線要求,最高工作溫度為125℃。
           
          Product Details 產品明細
          Model
          牌號
          Application
          用途
          W-2597 >0.5mm2 cables
          0.5mm2以上規格的電線
          W-2598 ≤ 0.5mm2 cables
          0.5mm2及以下規格的電線
           
           
           
           
          Processing Indicator 加工工藝
          Recommend to use single-screw extruders with L/D= 20-25.
          建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          Molding Temperature
          機頭溫度
          W-2597 165-185℃ 180-190℃
          W-2598 165-185℃ 185-195℃
           
           
          Physical and Electrical Properties 機械物理性能及電性能指標

          Item

          試驗項目

          Unit
          單位
          Technical Requirements
          技術要求
          W-2597 W-2598
          Density
          比重
          \ 1.34±0.02 1.34±0.02
          Tensile Strength
          拉伸強度
          MPa ≥18.0 ≥18.0
          Elongation at Break
          斷裂伸長率
          % ≥150 ≥150
          200℃Thermal Stability
          200℃時熱穩定時間
          min ≥360 ≥360
          20℃Volume Resistivity
          20℃時體積電阻率
          Ω.m ≥1×1011 ≥1×1011
          Brittle Temperature with Impact
          沖擊脆化溫度
          -25 -25
          Hardness
          硬度
          Shore A 94±2 97±2
          Thermal Aging
          熱老化試驗
          \ 155±3℃×240h
          Tensile Strength Variation
          拉伸強度變化率
          % ±20 ±20
          Elongation Variation
          斷裂伸長率變化率
          % ±20 ±20