          您所在的位置:網站首頁 > > 產品中心 > 通用PVC材料 > PVC特種料環保型聚氯乙烯耐遷移料 W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
          環保型聚氯乙烯耐遷移料 W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
          Lead-free Migration Resistant PVC Compound...
          型號:0

          參考價:¥

          說明:如您對該產品感興趣,請在此輸入您的手機號將本產品的地址 發送至您手機上。
          Product Description產品描述
          Lead-free migration resistant PVC compounds are granule compounds which are manufactured with mixing, plasticizing and pelletizing processes. They regard advanced PVC resin as the basic raw material, and add special plasticizer, stabilizer and other accessory ingredients.
          環保型聚氯乙烯耐遷移料是以優質聚氯乙烯樹脂為基料,加入特種增塑劑、特種穩定劑等助劑,經混合、塑化、造粒而成的粒狀電纜料。
           
          Characteristics and Application 特點及用途
          The products have excellent migration-resistant properties and good processability. They can meet RoHS Standard. They are mainly used for the jacketing of wire and cables which have anti-PS or anti-ABS property requirements.
          產品具有良好的非遷移性,加工性能優異,符合RoHS環保標準。主要用于耐PS或ABS電線電纜絕緣和護套。
           
          Processing Indicator加工工藝
          Recommend to use single-screw extruders with L/D= 20-25.
          建議使用普通長徑比為20-25的單螺桿擠出機進行生產。
          Model
          牌號
          Machine Barrel Temperature
          機筒溫度
          Molding Temperature
          機頭溫度
          W-7091 / W-9091 / W-0591 150-175℃ 170-185℃
          W-7092 / W-9092 / W-0592 150-175℃ 170-180℃
           
           
          Physical and Electrical Properties
          機械物理性能及電性能指標

          Item

          試驗項目

          Unit
          單位
          Technical Requirements
          技術要求
          W-7091 W-7092 W-9091 W-9092 W-0591 W-0592
          Tensile Strength
          拉伸強度
          MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
          Elongation at Break
          斷裂伸長率
          % ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
          Thermal Deformation
          熱變形
          % ≤40 ≤50 ≤40 ≤50 ≤40 ≤50
          Brittle Temperature with Impact
          沖擊脆化溫度
          -15 -20 -15 -20 -15 -20
          200℃Thermal Stability
          200℃時熱穩定時間
          min ≥60 ≥60 ≥80 ≥80 ≥80 ≥80
          20℃Volume Resistivity
          20℃時體積電阻率
          Ω.m ≥1.0×1011 ≥1.0×108 ≥1.0×1011 ≥1.0×109 ≥1.0×1011 ≥1.0×109
          Dielectric Strength
          介電強度
          MV/m ≥20 ≥18 ≥20 ≥18 ≥20 ≥18
          Thermal Aging
          熱老化試驗
          \ 100℃×168h 100℃×168h 100℃×240h 100℃×240h 135℃×168h 135℃×168h
          Tensile strength after aging
          老化后拉伸強度
          MPa ≥15.0 ≥15.0 ≥15.0 ≥15.0 ≥16.0 ≥16.0
          Tensile Strength Variation
          拉伸強度變化率
          % ±20 ±20 ±20 ±20 ±20 ±20
          Elongation After Aging
          老化后斷裂伸長率
          % ≥150 ≥180 ≥150 ≥180 ≥150 ≥180
          Elongation Variation
          斷裂伸長率變化率
          % ±20 ±20 ±20 ±20 ±20 ±20
          Migration ResistantTest
          耐遷移試驗
          (55℃×168h)
          \ 無污染 無污染 無污染 無污染 無污染 無污染